NIZHNEKAMSKNEFTEKHIM PE 4116Q (16403) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 4116Q (16403) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.914 - 0.918 g/cc | 0.0330 - 0.0332 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 2.6 - 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.6 - 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 78 - 96 g/10 min @Load 21.6 kg, Temperature 190 °C |
78 - 96 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 45.0 MPa | >= 6530 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 25.0 MPa | >= 3630 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 500 % | >= 500 % | ASTM D882 |
| Film Elongation at Break, TD | >= 870 % | >= 870 % | ASTM D882 |
| Tensile Modulus | >= 0.110 GPa | >= 16.0 ksi | 2% sec, MD; ASTM D882 |
| >= 0.110 GPa | >= 16.0 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 3.74 g/micron | >= 95.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 14.2 g/micron | >= 360 g/mil | ASTM 1922 |
| Dart Drop Test | >= 80.0 g | >= 0.176 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJJC330 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nylene® 7139 (HS) Low Wear Nylon 6/6
- Hexcel® HexWeb® CR III 3/8-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Dow Corning CE 0101 WIPES LOTION
- ExxonMobil Label-Lyte™ 35LL400 OPP Film
- Entec Hypro™ PP-CP10/2 Impact Copolymer, 10 Melt Flow, Nucleated, Anti-stat
- Ascend Performance Materials Vydyne® R543H Black Nylon 66, 43% Glass Reinforced, DAM
- Pau Tai #401, Modifier for PVC
- Formosa Plastics Formolene® 4111T Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved