Borealis Daplen™ EG203AE Polypropylene Compound Elastomer and Mineral Modified

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EG203AE Polypropylene Compound Elastomer and Mineral Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EG203AE is a 20% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EG203AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EG203AE has been developed for rocker panels and exterior trims.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Borealis Method
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 230 °C
25 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133/12
Mechanical Properties Metric English Comments
Tensile Strength, Yield 15.00 MPa
2176 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 6.0 %
6.0 %
At 50 mm/min; ISO 527-2
Flexural Modulus 1.25 GPa
181 ksi
At 5 mm/min; ISO 178
Izod Impact, Notched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
ISO 180/1A
4.50 kJ/m²

@Temperature -20.0 °C
2.14 ft-lb/in²

@Temperature -4.00 °F
ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 3.50 J/cm²
16.7 ft-lb/in²
ISO 179/1eA
0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature 20.0 °C
27.8 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ISO 75-2
Shrinkage 0.100 %

@Temperature 90.0 °C,
Time 7200 sec
0.100 %

@Temperature 194 °F,
Time 2.00 hour
Post Shrinkage; Borealis Method
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F