Dow DOWLEX™ 2036G Linear Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name DOWLEX™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DOWLEX™ 2036G Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Improved thermal stability for high stiffness film applications Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
ASTM D792
Thickness 25.4 microns
1.00 mil
Melt Flow 2.5 g/10 min
2.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 16.9 MPa
2450 psi
ASTM D882
Film Tensile Strength at Yield, TD 17.59 MPa
2551 psi
ASTM D882
Film Elongation at Break, MD 623 %
623 %
ASTM D882
Film Elongation at Break, TD 754 %
754 %
ASTM D882
Impact 125
125
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
3720
3720
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
3910
3910
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
Elmendorf Tear Strength MD 83 g
83 g
ASTM D1922
Elmendorf Tear Strength TD 286 g
286 g
ASTM D1922
Elmendorf Tear Strength, MD 3.27 g/micron
83.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 11.3 g/micron
286 g/mil
ASTM D1922
Dart Drop Test 57.0 g
0.126 lb
Method A; ASTM D1709
Film Tensile Strength at Break, MD 59.21 MPa
8587 psi
ASTM D882
Film Tensile Strength at Break, TD 39.91 MPa
5788 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
Dow Method (DSC)
Vicat Softening Point 119 °C
246 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 2.6 %
2.6 %
ASTM D1003
Gloss 90 %
90 %
45°; ASTM D2457