SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
1.39 g/cc
0.0502 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.00080 cm/cm

@Time 86400 sec
 0.00080 in/in

@Time 24.0 hour
 ISO 294
0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0049 cm/cm

@Time 86400 sec
 0.0049 in/in

@Time 24.0 hour
 ISO 294
0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
ISO 527
201 MPa
29200 psi
ASTM D 638
Tensile Strength, Yield 194 MPa
28100 psi
ISO 527
201 MPa
29200 psi
ASTM D 638
Elongation at Break 1.3 %
1.3 %
ISO 527
1.4 %
1.4 %
ASTM D 638
Elongation at Yield 1.2 %
1.2 %
ISO 527
1.4 %
1.4 %
ASTM D 638
Tensile Modulus 18.79 GPa
2725 ksi
1 mm/min; ISO 527
21.37 GPa
3099 ksi
50 mm/min; ASTM D 638
Flexural Strength 265 MPa
38400 psi
ISO 178
268 MPa
38900 psi
ASTM D 790
Flexural Modulus 15.16 GPa
2199 ksi
ASTM D 790
15.4 GPa
2230 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm

@Temperature 23.0 °C
 0.787 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.69 J/cm

@Temperature 23.0 °C
 8.79 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 27.0 kJ/m²

@Temperature 23.0 °C
 12.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
29.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.67 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
12.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 7.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 213 °C
415 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
211 °C

@Thickness 3.20 mm
 412 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
206 °C

@Thickness 3.20 mm
 403 °F

@Thickness 0.126 in
 unannealed; ASTM D 648