Beijing Chemical Industry KAIFA® MN301-M30 Nylon 66 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® MN301-M30 Nylon 66 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 33.0 kV/mm @Thickness 2.00 mm |
838 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.018 @Frequency 1e+6 Hz |
0.018 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 265 °C | 428 - 509 °F | |
| Middle Barrel Temperature | 260 - 265 °C | 500 - 509 °F | |
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Nozzle Temperature | 260 - 265 °C | 500 - 509 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 - 100 MPa | 8700 - 14500 psi |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1201-15 Polyester SMC
- Pyrotek Pyrocast HD Castable Refractory
- DSM Arnitel® EB500 50 Shore D, Blow Molding Grade Copolyester Elastomer (North America) (discontinued **)
- Westlake Plastics Tempalux® Polyetherimide
- Fainplast Compounds GA 67/K Flexible PVC, Flame Retardant Sheathing
- Fainplast Compounds CKL 59/OP Flexible PVC, Sheathing Lead Free
- American Polymers API 550 Polystyrene
- Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA) (Unverified Data**)
- Henkel Turco 6813 ED Paint Remover
Copyright © lookpolymers.com All Rights Reserved