SABIC Innovative Plastics LNP Stat-kon DX96690 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DX96690 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX96690 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0038 cm/cm @Time 86400 sec |
0.0038 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | ISO 527 |
| 112 MPa | 16200 psi | ASTM D 638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D 638 | |
| Tensile Modulus | 8.48 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 9.30 GPa | 1350 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 163 MPa | 23600 psi | ISO 178 |
| 176 MPa | 25500 psi | ASTM D 790 | |
| Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
| 8.58 GPa | 1240 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.89 J/cm @Temperature 23.0 °C |
7.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 35.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Gouda Vuurvast AC 90-5 D Dense Refractory Brick
- Kostat ICP-STAT ICS-1002 PP Sheet
- Industrial Laminates/Norplex MC511A Glass Fabric
- H.C. Starck Grade D Titanium Carbonitride
- SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer
- Techmer ES Electrafil® J-4/25/CF/15 NAT PA6/12
- The NanoSteel® Company SHS 9172 HVOF Steel Alloy, Atomized Powder
Copyright © lookpolymers.com All Rights Reserved