Beijing Chemical Industry KAIFA® HN301-M30 PA6 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® HN301-M30 PA6 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz |
0.024 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 210 °C | 392 - 410 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Nozzle Temperature | 235 - 240 °C | 455 - 464 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 - 90.0 MPa | 8700 - 13100 psi |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FRG20 Modified-PPO, V-1 Flame Retardant, 20% Glass Reinforced
- NOVA Chemicals Dylark® 510XT Glass Reinforced Engineering Resin
- Kennametal Stellite Deloro® 30 Nickel Alloy
- Michelman® Michem® Lube 135 Anionic paraffin/polyethylene wax emulsion
- Iran Petrochemical (PCC) TPC - 600 EX Expandable Polystyrene
- Lucite International Diakon® CLH952L Acrylic Polymer
- Multibase Multi-Flex® D 5304 Black TPO Thermoplastic Polyolefin Elastomer
- TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) CWSR
- Epoxyset Epoxibond EB-103F Unfilled Epoxy Adhesive
- Azoty Tarnow™ TARFLEN SG-2 PTFE
Copyright © lookpolymers.com All Rights Reserved