Aleris 55HX® Aluminum (5005-H14)

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Aleris
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aleris 55HX® Aluminum (5005-H14).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Used in interior and exterior architectural applications such as façades and claddings, ceilings and walls, and roofs. Attributes include: anodizing free of streaks; color uniformity between product batches; excellent flatness; very good deformation and bending properties; after anodizing, weather, corrosion and UV-resistant; scratch-resistant.
Physical Properties Metric English Comments
Density 2.70 g/cc
0.0975 lb/in³
AA 5005
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 145 - 185 MPa

@Thickness 0.200 - 1.50 mm
21000 - 26800 psi

@Thickness 0.00787 - 0.0591 in
145 - 185 MPa

@Thickness 1.50 - 3.00 mm
21000 - 26800 psi

@Thickness 0.0591 - 0.118 in
145 - 185 MPa

@Thickness 3.00 - 5.00 mm
21000 - 26800 psi

@Thickness 0.118 - 0.197 in
Tensile Strength, Yield >= 120 MPa

@Strain 0.200 %,
Thickness 0.200 - 1.50 mm
>= 17400 psi

@Strain 0.200 %,
Thickness 0.00787 - 0.0591 in
>= 120 MPa

@Strain 0.200 %,
Thickness 1.50 - 3.00 mm
>= 17400 psi

@Strain 0.200 %,
Thickness 0.0591 - 0.118 in
>= 120 MPa

@Strain 0.200 %,
Thickness 3.00 - 5.00 mm
>= 17400 psi

@Strain 0.200 %,
Thickness 0.118 - 0.197 in
Elongation at Break >= 2.0 %

@Thickness 0.200 - 1.50 mm
>= 2.0 %

@Thickness 0.00787 - 0.0591 in
>= 3.0 %

@Thickness 1.50 - 3.00 mm
>= 3.0 %

@Thickness 0.0591 - 0.118 in
>= 4.0 %

@Thickness 3.00 - 5.00 mm
>= 4.0 %

@Thickness 0.118 - 0.197 in
Modulus of Elasticity 68.9 GPa
10000 ksi
AA 5005
Poissons Ratio 0.33
0.33
AA 5005
Shear Modulus 25.9 GPa
3760 ksi
AA 5005
Thermal Properties Metric English Comments
CTE, linear 23.8 µm/m-°C

@Temperature 20.0 - 100 °C
13.2 µin/in-°F

@Temperature 68.0 - 212 °F
AA 5005
Specific Heat Capacity 0.900 J/g-°C
0.215 BTU/lb-°F
Thermal Conductivity 200 W/m-K
1390 BTU-in/hr-ft²-°F
AA 5005
Melting Point 632 - 654 °C
1170 - 1210 °F
AA 5005
Solidus 632 °C
1170 °F
AA 5005
Liquidus 654 °C
1210 °F
AA 5005
Component Elements Properties Metric English Comments
Aluminum, Al 97 - 99.5 %
97 - 99.5 %
As balance
Chromium, Cr <= 0.10 %
<= 0.10 %
Copper, Cu <= 0.20 %
<= 0.20 %
Iron, Fe <= 0.70 %
<= 0.70 %
Magnesium, Mg 0.50 - 1.1 %
0.50 - 1.1 %
Manganese, Mn <= 0.20 %
<= 0.20 %
Other, each <= 0.050 %
<= 0.050 %
Other, total <= 0.15 %
<= 0.15 %
Silicon, Si <= 0.30 %
<= 0.30 %
Zinc, Zn <= 0.25 %
<= 0.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000332 ohm-cm

@Temperature 20.0 °C
0.00000332 ohm-cm

@Temperature 68.0 °F
AA 5005