Beijing Chemical Industry KAIFA® HN301-G30 PA6 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® HN301-G30 PA6 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.280 J/cm @Thickness 3.20 mm |
0.525 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.023 @Frequency 1e+6 Hz |
0.023 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 220 °C | 410 - 428 °F | |
| Middle Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Nozzle Temperature | 240 - 245 °C | 464 - 473 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 600 A Zip 22 Natural Polyamide 6 Alloy (Nylon 6 Alloy)
- Phillips 66 COPYLENE® CH180V Polypropylene, Homopolymer, BCF, UV, Gas Fading
- KKPC KOSYN KTR 301 Thermoplastic Elastomer (TPE)
- Menzolit Menzolit® SMC 0400 Unsaturated Polyester UP
- Borealis HE3366 High Density Polyethylene
- A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene
- ELASTO UK Dryflex® 400701S SBS Based Material, 70A Hardness, Natural
- BASF Lucalen® A 3120 M Ethylene/Acrylate Copolymer
- BASF Neopolen® P 9230 K 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- BASF Capron® 8260 40% Mineral-Filled Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved