- Sumitomo Bakelite Durez® 22257 Phenolic, Injection Grade
Sumitomo Bakelite Durez® 22257 Phenolic, Injection Grade
| Category | Polymer , Thermoset , Phenolic , Phenolic, Novolac, Impact Grade, Filled |
| Manufacturer | Sumitomo Bakelite High Peformance Plastics |
| Trade Name | Durez® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite Durez® 22257 Phenolic, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Durez 22257 Black Phenolic is a two-stage, asbestos-free, medium impact molding material. It is designed for appliance and electrical applications where additional mechanical strength is required. Typical applications include circuit breakers, small motor bases and housings, appliance panels, terminal blocks, barrier strips, etc.Durez 22257 is fungus resistant per Mil-I-631D and Mil-810 A/E-2572Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.570 g/cc | 0.0206 lb/in³ | ASTM D1895 |
| Water Absorption | 0.60 % | 0.60 % | ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Shear Strength | 76.0 MPa | 11000 psi | as molded |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 42.2 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.4 µin/in-°F @Temperature 73.4 - 140 °F |
|
| Specific Heat Capacity | 1.42 J/g-°C | 0.339 BTU/lb-°F | |
| Thermal Conductivity | 0.402 W/m-K | 2.79 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL temperature Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.5 @Frequency 1e+6 Hz |
5.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 7.90 kV/mm | 201 kV/in | Step by step; ASTM D149 |
| 8.90 kV/mm | 226 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.080 @Frequency 1e+6 Hz |
0.080 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Radici Radilon® S RV200 (cond.) Nylon 6
- NOVA Chemicals Dytherm® 370R Expandable Polystyrene
- Mid-Mountain Materials ARMATEX® SRS 40 Silica Fabric Impregnated with Silicone Rubber
- SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-330 (HAF)
- DuPont™ Appeel® 72D799 Sealing Resin
- Fainplast Compounds HL 96/2 Flexible PVC, Insulation for High Temperatures
- Beijing Evergrow Resources ACFC800 Activated Carbon Fiber Cloth
Copyright © lookpolymers.com All Rights Reserved