BASF Ultramid® A3EG5 25% Glass Filled PA66 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® A3EG5 25% Glass Filled PA66 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Glass fiber reinforced injection molding grade for machinery components and housings of high stiffness and dimensional stability such as coil formers and bearing cages. Also used for electrically insulating parts.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.32 g/cc	0.0477 lb/in³	ISO 1183
Water Absorption	5.7 - 6.3 %	5.7 - 6.3 %	ISO 62
Moisture Absorption at Equilibrium	1.7 - 2.1 %	1.7 - 2.1 %	ISO 62
Viscosity Measurement	145	145	ISO 307
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in
Linear Mold Shrinkage, Flow	0.0048 cm/cm	0.0048 in/in	ISO 2577
	0.0055 cm/cm	0.0055 in/in	TM=300°C, TW=80°C
Linear Mold Shrinkage, Transverse	0.0106 cm/cm	0.0106 in/in	ISO 2577
Melt Flow	66 g/10 min @Load 5.00 kg, Temperature 275 °C	66 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	175 MPa	25400 psi	ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	ISO 527-1/-2
Modulus of Elasticity	8.60 GPa	1250 ksi	ISO 527-1/-2
Flexural Strength	260 MPa	37700 psi	ISO 178
Flexural Modulus	7.60 GPa	1100 ksi	ISO 178
Izod Impact, Notched (ISO)	9.50 kJ/m² @Temperature 23.0 °C	4.52 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	6.50 J/cm² @Temperature 23.0 °C	30.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	4300 MPa @Strain <=0.500 %	624000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 - 35.0 µm/m-°C @Temperature 23.0 - 80.0 °C	13.9 - 19.4 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	60.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C	33.3 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
Thermal Conductivity	0.340 W/m-K	2.36 BTU-in/hr-ft²-°F	DIN 52612-1
Melting Point	260 °C	500 °F	ISO 11357-1/-3
Maximum Service Temperature, Air	135 °C	275 °F	for 50% loss of tensile strength after 5000hr
	165 °C	329 °F	for 50% loss of tensile strength after 20000hr
	240 °C	464 °F
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 527-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	ISO 527-1/-2
Decomposition Temperature	>= 310 °C	>= 590 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.014 @Frequency 1.00e+6 Hz	0.014 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	550 V	550 V	Test Solution A; IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	290 °C	554 °F	Feed zone
Zone 2	290 °C	554 °F	Compression
Zone 3	290 °C	554 °F	Metering-zone
Zone 4	290 °C	554 °F	Nozzle
Melt Temperature	280 - 300 °C	536 - 572 °F	Injection Molding/Extrusion
	290 °C	554 °F	Optimal
Mold Temperature	80.0 °C	176 °F	Optimal
	80.0 - 90.0 °C	176 - 194 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %	Optimal
	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Commercial Status	Europe
Ignition Temperature	>400°C	ASTM D1929
Peripheral screw speed	< 0.3 m/s