BASF Ultraform® N2320 0035 LEV POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2320 0035 LEV POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM, rapidly solidifying standard grade with improved impact strength for injection moldingInformation provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO 2577 |
| Melt Flow | 10.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
10.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa @Load 36.5 kg, Time 30.0 sec |
18900 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 33 % | 33 % | Nominal, 50 mm/min; ISO 527-2 |
| Elongation at Yield | 12.5 % | 12.5 % | 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 2.45 GPa | 355 ksi | ISO 527-2 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 6.50 kJ/m² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 19.0 J/cm² @Temperature -30.0 °C |
90.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 26.0 J/cm² @Temperature 23.0 °C |
124 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.650 J/cm² @Temperature 23.0 °C |
3.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa @Strain <=0.500 % |
145000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 167 °C | 333 °F | DIN 53765 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-2 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 °C | 392 °F | Optimal |
| 190 - 230 °C | 374 - 446 °F | Injection-molding | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding |
| 90.0 °C | 194 °F | Optimal | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 3 hour | 3 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 320-340 °C | ASTM D1929 |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Victrex® APTIV® 1102-050M Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline, 20% Mineral Filled
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR Polyfil HG90 Filler
- Fine Organics FINALUX GT 25 Composite Lubricant
- Lanxess Durethan® BKV 35 H2.0 EF 901510 Nylon 6, 35% Glass Fiber
- SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific)
- Trelleborg AEM Eccofloat® EL-36/7300 Syntactic Foam
- Chi Mei Kibipol® PR-225 Butadiene Rubber (LBR)
- Entec Hylex® P1010FR Polycarbonate
- Fainplast Compounds PG 60 Flexible PVC, Extrusion Modified with Rubber
- Dow Corning 2-9148 RESIN
Copyright © lookpolymers.com All Rights Reserved