Techmer ES Elastoblend® PA6/6 HI BK Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 HI BK Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubricant and Impact ModifiedUl File Number: E157318Appearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % @Time 86400 sec |
1.3 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 48 % | 48 % | ASTM D638 |
| Flexural Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 1.82 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
3.40 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 8.54 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
16.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NX9250 PTFE Laminate, Woven-Glass Reinforced
- ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin (discontinued **)
- Industrial Laminates/Norplex ES-3 Engraving Stock
- Teknor Apex Monprene® MP-1479 Thermoplastic Elastomer
- Plastics Group Polifil® M-20 20% Mica-Reinforced Polypropylene
- Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified
- ConocoPhillips Hydroclear® V Automatic Transmission Fluid
- Axion Polymers Axpoly® PP06 5001 Enhanced Black General Purpose Polypropylene
- Addiplast Addinyl B2 ZV20 Nylon 6, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved