Kolon KOPA® KN173HI4 High Impact Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN173HI4 High Impact Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.013 - 0.016 cm/cm | 0.013 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7680 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 300 % | 300 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 78.5 MPa | 11400 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 1.81 GPa | 263 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 11.8 J/cm | 22.0 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 220 °C | 428 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Consil®-A 897 Silver-Aluminum Filled Silicone Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP (Asia Pacific)
- Samsung Cheil Industries Infino® HI-1001B PC/ABS, Unreinforced
- Tipco Tipcolene® SEB 300 - 30% Chemically Coupled Glass Fiber Polypropylene Homopolymer with High Heat Stability
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- UBE UBEPOL VCR303 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- ELASTO UK Dryflex® 500350S SEBS Based Material, Unfilled Qualities, 35A Hardness, Translucent
- Addcomp PRIEX® 12031 Maleic Anhydride Grafted HDPE
- 3M Scotchlite™ S60/10000 Glass Bubbles
- A. Schulman LP477-01 High-Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved