BASF Ultraform H 2320 006 Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform H
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform H 2320 006 Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform H2320 006 is a high-molecular-weight grade of POM for injection molding. It conforms to FDA requirements of 21 CFR 177.2470.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.020 cm/cm
0.020 in/in
ASTM Data; MD
Linear Mold Shrinkage, Flow 0.021 cm/cm
0.021 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ISO Data
Melt Flow 2.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 64.0 MPa
9280 psi
50mm/min; ISO 527
64.0 MPa
9280 psi
2 in/min; ASTM Test
33.0 MPa

@Temperature 80.0 °C
4790 psi

@Temperature 176 °F
ISO Data
Elongation at Break 30 %
30 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 11 %
11 %
50mm/min; ISO 527
11 %
11 %
2 in/min; ASTM Test
10 %

@Temperature 80.0 °C
10 %

@Temperature 176 °F
ISO Data
Tensile Modulus 2.59 GPa
376 ksi
ASTM Test
2.60 GPa
377 ksi
1mm/min; ISO 527
Flexural Modulus 2.45 GPa
355 ksi
ASTM Test
2.60 GPa
377 ksi
ISO Data
Izod Impact, Notched 0.694 J/cm

@Temperature -40.0 °C
1.30 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.801 J/cm

@Thickness 3.17 mm
1.50 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO Test
5.00 kJ/m²

@Temperature -40.0 °C
2.38 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 26.0 J/cm²
124 ft-lb/in²
ISO 179
20.0 J/cm²

@Temperature -30.0 °C
95.2 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
0.550 J/cm²

@Temperature -30.0 °C
2.62 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Tensile Creep Modulus, 1 hour 1800 MPa
261000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 1300 MPa
189000 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
33.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359
Melting Point 166 °C
331 °F
10 K/min
166 °C
331 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 154 °C
309 °F
ASTM Test
156 °C
313 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75
96.0 °C
205 °F
ASTM Test
Vicat Softening Point 150 °C
302 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Oxygen Index 15 %
15 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 200 °C
392 °F
Injection molding
Mold Temperature 110 °C
230 °F
Injection molding
Injection Velocity 90.0 mm/sec
3.54 in/sec
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
NSF Std. 61 Yes
Primary Processing Technique Extrusion
Processing Injection Molding
Other Extrusion
Special characteristic Release agent