Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Dry)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications include electrical and electronic components.Features: Fast Molding Cycle; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Strength; Hot Water Moldability; Low Moisture Absorption; LubricatedUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Cell Phones; Electrical/Electronic Applications; General Purpose; Housings; Industrial Applications; Machine/Mechanical Parts; Metal Replacement; Power/Other Tools; Thick-walled Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA105G35Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
1.45 g/cc
0.0524 lb/in³
ASTM D792
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.29 %

@Time 86400 sec
0.29 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ASTM D638
Elongation at Break 2.5 %
2.5 %
ASTM D638
Tensile Modulus 11.7 GPa
1700 ksi
ASTM D638
Flexural Yield Strength 290 MPa
42100 psi
ASTM D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D790
Compressive Strength 179 MPa
26000 psi
ASTM D695
Poissons Ratio 0.41
0.41
ASTM E132
Shear Strength 90.0 MPa
13100 psi
ASTM D732
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.60 J/cm
18.0 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C

@Temperature 150 - 250 °C
7.78 µin/in-°F

@Temperature 302 - 482 °F
2
22.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
12.2 µin/in-°F

@Temperature 32.0 - 194 °F
2
CTE, linear, Transverse to Flow 59.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
32.8 µin/in-°F

@Temperature 32.0 - 194 °F
TMA; ASTM E831
120 µm/m-°C

@Temperature 100 - 250 °C
66.7 µin/in-°F

@Temperature 212 - 482 °F
TMA; ASTM E831
Melting Point 327 °C
621 °F
DSC
327 °C
621 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 320 °C

@Thickness 3.20 mm
608 °F

@Thickness 0.126 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 300 °C

@Thickness 3.20 mm
572 °F

@Thickness 0.126 in
Annealed; ASTM D648
Flammability, UL94 HB

@Thickness 3.18 mm
HB

@Thickness 0.125 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
UL 746
High Voltage Arc-Tracking Rate, HVTR 14.0 mm/min
0.551 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 318 - 324 °C
604 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 329 - 343 °C
624 - 649 °F
Drying Temperature 120 - 135 °C

@Time 14400 sec
248 - 275 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Lubricant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Processing Technique Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant