Arlon 48571R005 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate (discontinued **)&l

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 48571R005 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate (discontinued **)&l.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Uncured RubberSide 2: Uncured RubberThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	>= 25.4 microns	>= 1.00 mil	Side 2
	>= 25.4 microns	>= 1.00 mil	Side 1
	38.1 microns	1.50 mil	Polyethylene Interleave
	50.8 microns	2.00 mil	Unprimed Coated 1080 Fiberglass (same as 108/no plied yarns), Substrate
	63.5 microns	2.50 mil	Primed Coated 1080 Fiberglass (same as 108/no plied yarns), Substrate
	114 - 165 microns	4.50 - 6.50 mil	Overall

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40 - 50	40 - 50	Compound Property
Tensile Strength	>= 5.52 MPa	>= 800 psi	Compound Property
Elongation at Break	>= 550 %	>= 550 %	Compound Property
Peel Strength	>= 0.701 kN/m	>= 4.00 pli	[ppi], Bond Strength

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
UL RTI, Electrical	220 °C	428 °F	per UL Card E54153
UL RTI, Mechanical without Impact	200 °C	392 °F	per UL Card E54153
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 177 °C	0.250 hour @Temperature 350 °F	Recommended Cure Cycle
	120 min @Temperature 232 °C	2.00 hour @Temperature 450 °F	Recommended Postcure Cycle
Shelf Life	6.00 Month @Temperature <=23.9 °C	6.00 Month @Temperature <=75.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	4.5 - 5.5
Uncoated Fabric Break Strength	40 lb/in	Fill Direction, Substrate Property
	70 lb/in	Warp Direction, Substrate Property