Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 70.3 MPa | 10200 psi | ASTM D638-95 |
Multibase Multi-Pro® 4008 RC Medium Impact 40% Glass Filled Polypropylene Multi-Pro 4008 RC is a chemically coupled glass reinforced polypropylene compound exhibiting highest flexural modulus, flex strength and high impact resistance. Heat resistance is high due to highl.. |
|||
Tensile Strength, Ultimate | 70.0 MPa @Temperature 90.0 °C |
10200 psi @Temperature 194 °F |
ISO 527 |
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G2 PC+ABS, 10% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 10% glass fibres, high stiffness, very good dimensional stability. Vicat/B50 = 135°C Main application field.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638-68 |
Budd DSM-971 Smooth Surface, Class "A" SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 70.0 - 80.0 MPa @Temperature 130 - 175 °C |
10200 - 11600 psi @Temperature 266 - 347 °F |
Average value: 66.6 MPa Grade Count:2 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 70.0 - 80.0 MPa @Time 1.80e+7 - 7.20e+7 sec |
10200 - 11600 psi @Time 5000 - 20000 hour |
Average value: 66.6 MPa Grade Count:2 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 70.3 MPa | 10200 psi | ASTM D638 |
Global 120-PC-Natural Acrylonitrile Styrene, General Purpose Grade Description-transparent, natural, medium impact resistance, high hardness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInformation provide.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
Lucite International Perspexâ„¢ XT Acrylic Extruded Sheet 0X00 PERSPEX extruded sheet has a lower molecular weight making it easy to vacuum form and the extrusion process gives excellent thickness tolerance and is economical for long production runs.Information.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | Safety factor of 10-20X is necessary in practice |
Saint-Gobain Vitreosil® Clear Fused Quartz Tubing Electrically fused quartz is recognized for its combination of purity, chemical inertness, physical stability, thermal shock resistance, high electrical resistivity, and high operating temperatures... |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber Injection molding grade, glass reinforced (16%).Applications: Automotive industry: instrument panels, rear light housings, internal components of domestic appliances. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Plenco 00732 Melamine-Phenolic, Granular, Injection Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Wellman Wellamid® 22LHI3 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Tipco Tipcolene® SEB 300 FR - UL94-V-0 Flame Retardant, 10% Chemically Coupled Glass Fiber Polypropylene Homopolymer 30% Glass Reinforced, Flame Retardant PP HomopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D882 |
DuPont Selar® PA 2072 Nylon Barrier Resin Selar® PA 2072 is an amorphous nylon (polyamide) resin which is specially designed for blending with ethylene vinyl alcohol (EVOH) copolymers. Selar® PA 2072 can be tumble-blended with most grades.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Covestro Makrolon® 8035 Polycarbonate High viscosity extrusion and injection molding grade with 30% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013G15 1 NA PA6-GF15 15% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
DSM Akulon® K224-G3-FC NA99001 PA6-GF15 15% Glass Reinforced |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
BASF Procom® GC20H 250 Polypropylene Uses: car and truck fans and shrouds, car rear light housings, car radiator expansion tanks, car grills, domestic appliance components (e.g. washing machine tanks, impellers housings, etc.), textile.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 |
BASF Ultramid® NFX-0102 NF2004 30% Glass Filled PA66 (Dry) Ultramid NFX-0102 NF2004 is a heat stabilized, 30% glass bead PA66 injection molding grade. It is especially formulated for low warp, increased stiffness and excellent dimensional stability. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ATSM D638 |
Ashley Polymers Ashlene® 851 Nylon 6, High Viscosity High viscosity for blown film, tubing, rods and shapes and blow molding. Has highest puncture resistance and clarity. FDA and NSF approved.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 132 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.45% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 - 255 MPa | 10200 - 37000 psi | Average value: 166 MPa Grade Count:88 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4040 G3 HT BK5830 15% Glass Filled PBT/PET Ultradur B 4040 G3 HT BK5830 is a 15% glass filled, pigmented black, injection molding PBT. It is a resin for molding household appliances and equipment which must be resistant to chemicals and oth.. |
|||
Tensile Strength, Ultimate | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 122 MPa Grade Count:71 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 663 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 - 100 MPa @Temperature -40.0 - -40.0 °C |
10200 - 14500 psi @Temperature -40.0 - -40.0 °F |
Average value: 85.0 MPa Grade Count:4 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |