Multibase Multi-Pro® 4008 RC Medium Impact 40% Glass Filled Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler
Manufacturer Multibase
Trade Name Multi-Pro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Pro® 4008 RC Medium Impact 40% Glass Filled Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Multi-Pro 4008 RC is a chemically coupled glass reinforced polypropylene compound exhibiting highest flexural modulus, flex strength and high impact resistance. Heat resistance is high due to highly coupled glass fiber matrix.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792-91
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955-89
Melt Flow 8.5 g/10 min
8.5 g/10 min
(Condition L) ASTM D-1238-94a
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
10 sec; ASTM D-2240-95
Tensile Strength, Ultimate 70.3 MPa
10200 psi
ASTM D638-95
Flexural Strength 113.3 MPa
16430 psi
ASTM D790-95
Flexural Modulus 6.345 GPa
920.3 ksi
Method 1, Proc. B; ASTM D-790-95
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256-93a
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ASTM D648-95
Deflection Temperature at 1.8 MPa (264 psi) 146 °C
295 °F
ASTM D648-95