- KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer
KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Korea Engineering Plastics Co., Ltd. |
| Trade Name | Kepital® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
injection molding: electrical parts, machine/mechanical parts, industrial parts, automotive applications, electronic data processing.Kepital® is a registered trademark of Korea Engineering Plastics Co., Ltd. Information provided by Dayson Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 45 g/10 min | 45 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 62.2 MPa | 9020 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.616 GPa | 379.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.491 J/cm | 0.920 ft-lb/in | 0.126 inches; ASTM D256 |
| Tensile Impact Strength | 98.1 kJ/m² | 46.7 ft-lb/in² | 0.0630 in; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 20.0 °C |
72.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0315 in. |
| HB | HB | 0.252 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 172 Tin Solder Alloy
- SABIC Innovative Plastics ULTEM 2200 PEI (Europe-Africa-Middle East)
- Silikony Polskie Polastosil M-200 Silicone Rubber
- Shakespeare NX-310 diameter 0.2 mm Nylon 66 Monofilament
- Master Bond EP19HT One Component, Storage Stable Epoxy System
- Loctite® 3106 Acrylic Light Cure Adhesive
- DSM Akulon® K225-KS Nylon 6 (European and Asian Grade) (Cond)
- EMS-Grivory Grivory® GM-4H PA*-MD40
- Chosun Refractories SCX-60KL Special SiC Castable
- Braskem Green PE SHC7260 Injection Molding High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved