Kolon KOPA® KN173HI2 High Impact Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN173HI2 High Impact Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.013 - 0.016 cm/cm | 0.013 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 58.8 MPa | 8530 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 250 % | 250 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm | 4.59 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 215 °C | 419 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 1725-xx13FRD Polyvinyl Chloride, Flexible (PVC, Flexible)
- Osprey Metals Co212-e Cobalt Alloy Powder (Grade 80% - 22)
- Lehmann & Voss LUVOCOM® 1105-7760 PEEK, with carbon fiber, PTFE, lubricant modified, high viscosity
- Karina E 805-48/1-IS-RG Black PVC Compound
- Shandong Dongyue Shenzhou New Material Co DS602 Perfluorinated Ethylene-Propylene Copolymer
- Shandong Rike Chemical HELIâ„¢ HG-200 PVC Processing Aid Series (PA)
- Saint-Gobain CHR® K100 Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66
- Covestro Bayfill® 361 Polyurethane Semi-Rigid Foam, Conventional Catalyst, Open Pour, MDI-based 2-Component Liquid System
- DuPont™ Appeel® 72D799 Sealing Resin
Copyright © lookpolymers.com All Rights Reserved