Samyang Trirex® 3030U Polycarbonate, UV Stabilized
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3030U Polycarbonate, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Applications:Specially suitable for weathering resistance (UV stabilized type)All information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 70.6 MPa | 10200 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
| Izod Impact, Unnotched | 9.32 J/cm @Thickness 3.17 mm |
17.4 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 56.0 µm/m-°C | 31.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.85 @Frequency 1.00e+6 Hz |
2.85 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.0092 @Frequency 1.00e+6 Hz |
0.0092 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 300 - 310 °C | 572 - 590 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Sibur ABS 2020-60 Molding Grade ABS Plastic
- Styron DL 2256LA Carboxylated SB
- EMS-Grivory Grivory® AG-30 PA66-GF30
- ChevronTexaco RPM® NLGI 2 Automotive LC Grease EP
- Chem Polymer Chemlon 130 GVH Nylon 66, 30% Glass Fiber Reinforced
- Cheng Yu Plastic FR200GV20 Flame Retardant Nylon 66, 20% Glass Fiber
- Total Lacqtene® 2001 TBK 40 HDPE pipe (discontinued **)
- Universal Wire Works 122 Nickel Alloy Welding Wire
Copyright © lookpolymers.com All Rights Reserved