LG Chemical LUCON PN9009 PPS+MF
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON PN9009 PPS+MF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Molding Grade, PPS+MF, High Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts (Heat sink, LED etc.) Motor HousingCAS No. 25212-74-2 and 7782-42-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.95 g/cc | 1.95 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm |
0.0040 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 320 °C |
40 g/10 min @Load 11.0 lb, Temperature 608 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
1mm/min; ASTM D790 |
| Flexural Modulus | 13.7 GPa @Thickness 6.40 mm |
1990 ksi @Thickness 0.252 in |
1mm/min; ASTM D790 |
| Izod Impact, Notched | 0.196 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.367 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 2.50 W/m-K | 17.4 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.40 mm |
500 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Middle Barrel Temperature | 310 - 320 °C | 590 - 608 °F | Injection Molding |
| Front Barrel Temperature | 320 - 325 °C | 608 - 617 °F | Injection Molding |
| Nozzle Temperature | 310 - 330 °C | 590 - 626 °F | Injection Molding |
| Melt Temperature | 330 °C | 626 °F | Resin, Injection Molding |
| Mold Temperature | 130 - 150 °C | 266 - 302 °F | Injection Molding |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Radici Raditer® BRV300 Polybutylene Terephthalate
- 1095A Polyurethane-based Biomedical Elastomer
- Chevron Phillips HiD® 9406 HDPE Blow Molding Resin (discontinued **)
- Fainplast Compounds RH 214 Rigid PVC, Antishock Extrusion
- Shamrock Technologies NanoFLON® P 40A Thermoplastic Grade PTFE Additive
- Hexcel® HexWeb® HRH-327 - 3/8 - 5.5 Fiberglass Reinforced Polyimide Honeycomb
- Entec Hypro™ PPC-CC40 Natural Copolymer Polypropylene, 40% Calcium Carbonate Filled
- Fainplast Compounds GA 75/3 Flexible PVC, Flame Retardant Sheathing
- Solvay Specialty Polymers Ryton® V-1 Polyphenylene Sulfide Coating Resin (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved