Shinkong Synthetic Fibers Shinite® D202 PBT, Fire Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® D202 PBT, Fire Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.019 cm/cm | 0.0060 - 0.019 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.019 cm/cm | 0.0060 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 58.8 MPa | 8530 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 | 3.0 | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- MarkeTech Indium Phosphide Semiconductor Wafer, p-type, Zinc Doped, Czochralski-LEC Grown
- KaMin Polyfil® HG90 Kaolin Clay - Waterwashed
- SABIC Innovative Plastics LNP LUBRICOMP LX00430 PEEK
- Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle
- Channel Industries 300 Barium Titanate Piezoelectric
- Aclo Accutech Polypropylene Homopolymer HP0339T10L Talc Reinforced
- 3M 501+ Specialty High Temperature Masking Tape
- 3M FM041902 White Polyester Label Products
- Beijing Evergrow Resources PTFE, 24% Bronze, 12% Glass Fiber, 6% Graphite Filled
Copyright © lookpolymers.com All Rights Reserved