Bhansali Engineering Abstron IMG1120 Glass Reinforced Grade

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron IMG1120 Glass Reinforced Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D-792
Filler Content 20 %
20 %
Glass
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ASTM D-955
Melt Flow 12 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 12 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D-785
Tensile Strength, Yield 61.8 MPa

@Thickness 3.20 mm
 8960 psi

@Thickness 0.126 in
 Type 1, 5 mm/min; ASTM D-638
Flexural Yield Strength 88.3 MPa

@Thickness 6.40 mm
 12800 psi

@Thickness 0.252 in
 ASTM D-790
Flexural Modulus 4.12 GPa

@Thickness 6.40 mm
 597 ksi

@Thickness 0.252 in
 ASTM D-790
Izod Impact, Notched 0.588 J/cm

@Thickness 6.40 mm
 1.10 ft-lb/in

@Thickness 0.252 in
 ASTM D-256
0.686 J/cm

@Thickness 3.20 mm
 1.29 ft-lb/in

@Thickness 0.126 in
 ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 115 °C
239 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 UL-94