Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-2 |
PolyOne Nymax™ 2024 HS UV 425C Grey Polyamide 66 (Nylon 66) The Nymax® Series of nylon 6/6 compounds have been specifically developed to deliver outstanding performance in a wide range of application areas. These materials are available with a broad range o.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers Opnyl OP66UT108 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min |
Polimeri Europa KOBLEND HI 40 PBT+PC, Impact Grade
(discontinued **) Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified blend PBT+PC blend with very good impact behaviour, ductility even at low temperatures, resistant to solvents, good dimensional stabilit.. |
|||
Tensile Modulus | 1.80 GPa @Temperature 100 °C |
261 ksi @Temperature 212 °F |
ISO 527 |
Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Ineos ABS Lustran® 743 General Purpose, High-Impact
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | |
Ineos ABS Lustran® QE 1110, Extrusion Grade
(discontinued **) Extrusion grade, for coextrusion to surfaces with extreme low gloss.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a ma.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | Conditioned 50% RH; ISO 527 |
Manifattura Cattaneo PA 6 G Nylon Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527-1,-2 |
Ineos ABS Lustran® ABS M406 Lustran® ABS M406 has very high impact strength and increased chemical and dynamic resistance. It is used for the production of molded plastic articles. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-1/-2 |
Styrolution Polystyrol 486 M GR 2 PS Description: Polystyrol 486 M is a normal flowing, high-impact grade that is especially suitable for blends with a high proportion of general-purpose Polystyrol (preferably Polystyrol 165 H or Polys.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP M7002XXH PP LNP* THERMOCOMP* M7002XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additives. Designed for touch surfaces in healthcare applications. Added features include:.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Total PS CPDS 815 High Flow, Non-Deca Polystyrene Total Petrochemicals Polystyrene 815 is a high heat resistant, high impact Polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensional stab.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-2 |
Total PPC 1645 Polypropylene, Heterophasic Copolymer, Pipes Polypropylene PPC 1645 is a nucleated heterophasic (block) copolymer with a Melt Flow index of 0.3 g/10 min. This resin has a long-term heat stabilization package. It offers a very high stiffness .. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
Polyram RamShine PV111 Acrylonitrile Butadiene Styrene General purpose ABS for injection molding applications.Information provided by Polyram. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Eastman Eastar DN010 Copolyester Eastar Copolyester DN010 is a brilliantly clear polymer having excellent impact strength, chemical resistance, and low shrinkage rates. Eastar Copolyester DN010 contains no mold release.Applications.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | Film M.D.; ASTM D882 |
Eastman Eastman Embrace Copolyester for Shrink Film Applications:Flexible packagingIV containersLabels to fit high contour containersShrink packagingWrap around designKey Attributes:Excellent clarityExcellent printabilityGood chemical resistanceGood .. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | Storage |
Epoxy Technology EPO-TEK® 320 Optical, Opaque Epoxy Product Description: EPO-TEK® 320 is a two component, black-colored and optically opaque epoxy designed for optical, medical, and optoelectronic packaging of semiconductor devices and components. .. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® ST7301 BK356 Nylon 6
(Unverified Data**) Super Toughened Polyamide 6 Zytel ST7301 BK356 is a Super Tough heat stabilized lubricated black polyamide 6 resin for injection molding and extrusion. It offers outstanding impact resistance over a.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436C40L Calcium Reinforced |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min |
Arkema Group Rilsan® AESN Y T6L Nylon 12, MoS2 Filled (Dry) Designation ISO 1874-PA12,EHLS,22-010,MD05Grade with molybdenum filler for extrusion. Available color: steel gray. Reinforced light and heat stabilizing agents.Low friction coefficient. No need of l.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437W30L Wollastonite Reinforced |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | |
BASF Polystyrol® 486 M Impact Grade Polystyrene (Europe) Normal flowing, high-impact grade that is especially suitable for blends with a high proportion of general-purpose Polystyrol (preferably Polystyrol 165 H). Suitable for dairy packaging.Data was co.. |
|||
Tensile Modulus | 1.80 GPa @Temperature 120 °C |
261 ksi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436T20L1 Talc Reinforced |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M10L Mica Reinforced |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339T20L1 Talc Reinforced |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527-2 |
Ascend Performance Materials Vydyne® 66J Nylon 66, General Purpose, high viscosity, Conditioned Vydyne® 66J is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66J resin offers high strength, .. |
|||
Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GS 20 HWCP 20% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |