- Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated
Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 - 0.90 % | 0.50 - 0.90 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | DIN 53453 |
| 5.00 J/cm² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- RheTech Products FT1003-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Noble Polymers Ecobarrier™ 0414 Thermoplastic Olefin (TPO)
- ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film (discontinued **)
- Materion Beryllium Copper Alloy M25 Wire; 1/2H (TD02) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Shin-Etsu Silicones KE-1842 Silicone, RTV Adhesive/Sealant
- Cytec EN-2527 (Conap) Potting and Encapsulation Adhesive
- Akro-Plastic Akromid® B3 GF 30 S1 NAT. (1383) PA, Cold-Impact Resistant, 30% Glass Filled, Natural
- BASF Ultradur® S 4090 G6X 30% Glass Filled PBT
- DuPont Elvax® 3134Q Ethylene-Vinyl Acetate Copolymer Resin for Extrusion Coating, Casting (discontinued **)&l