Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), High Impact
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistance combined with good mechanical property retention over a broad temperature/ humidity range. Possible applications for AMODEL ET-1001 L resin include anti-friction and wear resistant components, and components of chemical and oil processing equipment, sporting goods, automobiles, household appliances, power tools, and safety equipment, where exceptional impact strength and high modulus are required. AMODEL ET-1001 L resin contains a lubricant for easier processing with conventional equipment and methods.Information provided by Solvay Advanced Polymers
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ISO 1183A
1.15 g/cc
1.15 g/cc
ASTM D792
Moisture Absorption at Equilibrium 0.70 %
0.70 %
24 hours; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
ISO 527
31.0 MPa

@Temperature 100 °C
4500 psi

@Temperature 212 °F
ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
ISO 527
76.0 MPa
11000 psi
ASTM D638
32.0 MPa

@Temperature 100 °C
4640 psi

@Temperature 212 °F
ISO 527
Elongation at Break 15 %
15 %
ISO 527
30 %
30 %
ASTM D638
54.3 %

@Temperature 100 °C
54.3 %

@Temperature 212 °F
ISO 527
Elongation at Yield 6.0 %
6.0 %
ASTM D638
6.0 %
6.0 %
ISO 527
3.1 %

@Temperature 100 °C
3.1 %

@Temperature 212 °F
ISO 527
Tensile Modulus 2.30 GPa
334 ksi
ISO 527
2.40 GPa
348 ksi
ASTM D638
1.80 GPa

@Temperature 100 °C
261 ksi

@Temperature 212 °F
ISO 527
Flexural Strength 66.0 MPa
9570 psi
ISO 178
128 MPa
18600 psi
ASTM D790
42.0 MPa

@Temperature 100 °C
6090 psi

@Temperature 212 °F
ISO 178
Flexural Modulus 1.90 GPa
276 ksi
ISO 178
2.60 GPa
377 ksi
ASTM D790
1.30 GPa

@Temperature 100 °C
189 ksi

@Temperature 212 °F
ISO 178
Poissons Ratio 0.35
0.35
Shear Modulus 0.852 - 0.889 GPa
124 - 129 ksi
Calculated
Shear Strength 53.0 MPa
7690 psi
ASTM D732
Izod Impact, Notched 9.60 J/cm
18.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1U
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched NB
NB
ISO 179/1eA
Dynatup @ -18°C 43.0 J
31.7 ft-lb
Energy at Maximum Load. Dry as molded. 23°C; D3763
46.0 J
33.9 ft-lb
Energy at Maximum Load. Dry as molded. -23°C; D3763
64.0 J
47.2 ft-lb
Total Energy. Dry as molded. 23°C; D3763
66.0 J
48.7 ft-lb
Total Energy. Dry as molded. -23°C; D3763
Dynatup @ -18°C Max Load 571000 g
1260 lb
23°C; D3763
662000 g
1460 lb
-23°C; D3763
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ASTM D3418
310 °C
590 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
ISO 75Af
120 °C
248 °F
ASTM D648