Eastman Eastman Embrace Copolyester for Shrink Film

Category Polymer , Film , Thermoplastic , Polyester, TP
Manufacturer Eastman Chemical
Trade Name Eastman
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Eastman Embrace Copolyester for Shrink Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:Flexible packagingIV containersLabels to fit high contour containersShrink packagingWrap around designKey Attributes:Excellent clarityExcellent printabilityGood chemical resistanceGood gloss and sparkleGreater than 80% ultimate shrinkageHigh shrink forceShrinks to fit contour bottlesSuper-high print definitionProduct Description: Eastman Embrace copolyester is shrink film for dairy, water, juice, liquor, and sports and soft drink beverage packaging. Eastman Embrace copolyester provides excellent clarity, printability, and toughness, enabling marketers to increase shelf visibility, presence, and appeal for their products. With ultimate shrinkage of over 80%, Eastman Embrace copolyester is the ideal label material for marketers looking to differentiate their products in the competitive beverage market. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®. This Product has been CRADLE TO CRADLE CERTIFIEDcm Silver.Information provided by Eastman.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ASTM D1505
Water Vapor Transmission 20.0 g/m²/day
1.29 g/100 in²/day
ASTM F1249
Oxygen Transmission Rate 71.0 cc/m²/day

@Pressure 0.101 MPa,
Temperature 30.0 °C
4.57 cc/100 in²/day

@Pressure 14.7 psi,
Temperature 86.0 °F
68% RH; ASTM F1249
Viscosity Measurement 0.70
0.70
Inherent; EMN-A-AC-G-V-1
Thickness 50.0 microns
1.97 mil
Surface Tension 9.0 dynes/cm
9.0 dynes/cm
Harmonic Mean - Polar
38 dynes/cm
38 dynes/cm
Harmonic Mean - Dispersive
47 dynes/cm
47 dynes/cm
Harmonic Mean - Total
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 265 %
265 %
ASTM D882
Film Elongation at Break, TD 34 %
34 %
ASTM D882
Tensile Modulus 1.80 GPa
261 ksi
Film M.D.; ASTM D882
7.25 GPa
1050 ksi
Film T.D.; ASTM D882
Tear Strength, Total 0.120 N
0.0270 lb (f)
T.D., Elmendorf; ASTM D1922
1.20 N
0.270 lb (f)
M.D., Elmendorf; ASTM D1922
Dart Drop Test 228 g
0.503 lb
ASTM D1709A
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Break, TD 290 MPa
42100 psi
ASTM D882
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 71.0 °C
160 °F
ASTM D1525
Shrinkage 80 %

@Temperature 90.0 °C
80 %

@Temperature 194 °F
Ultimate
Optical Properties Metric English Comments
Haze 4.9 %
4.9 %
ASTM D1003
Gloss 139 %
139 %
at 60°; ASTM D2457
Transmission, Visible 85 %

@Thickness 0.0500 mm
85 %

@Thickness 0.00197 in
Transparency, Film; ASTM D1746
86 %

@Thickness 0.0500 mm
86 %

@Thickness 0.00197 in
Regular, Film; ASTM D1003
92 %

@Thickness 0.0500 mm
92 %

@Thickness 0.00197 in
Total, Film; ASTM D1003
Descriptive Properties Value Comments
Color 0.02
a*
0.37
b*
95.9
L*