Aclo Accutech Polypropylene Copolymer CP0437W30L Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W30L Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 53 | 53 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F |
Users viewing this material also viewed the following:
- RheTech Products T10P102-00EG 10% Talc Reinforced Polypropylene, Extrusion Grade, Natural
- SABIC Innovative Plastics Cycolac® GHT3330 ABS (Asia Pacific)
- Flint Hills P5G2N-093 Random Copolymer Polypropylene
- Westlake Plastics Pomalux® SD-A Acetal Copolymer (anti-static)
- Total PPC 5724 Polypropylene, Extra High Impact Copolymer
- Ensinger Tecapeek® XP-118 Compression Molded PEEK Compound, 20% Fiberglass with 5% PTFE
- Alliance Polymers Viprene™ G55A-32U-BLK Thermoplastic Vulcanizate Elastomer
- ATI Allegheny Ludlum AL 22™ Nickel-Base Alloy, UNS N06022
Copyright © lookpolymers.com All Rights Reserved