Total PPC 1645 Polypropylene, Heterophasic Copolymer, Pipes

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade
Manufacturer	Total Atofina
Trade Name	PPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 1645 Polypropylene, Heterophasic Copolymer, Pipes.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polypropylene PPC 1645 is a nucleated heterophasic (block) copolymer with a Melt Flow index of 0.3 g/10 min. This resin has a long-term heat stabilization package. It offers a very high stiffness while keeping good impact strength (even at very low temperatures) and excellent processability. Polypropylene PPC 1645 has been designed to allow pipe thickness reduction, resulting in cost savings.Polypropylene PPC 1645 can also be used for blow molding and other extrusion applications.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Oxidative Induction Time (OIT)	>= 10 min @Temperature 200 °C	>= 10 min @Temperature 392 °F	EN 728
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 230 °C	0.30 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	32.0 MPa	4640 psi	ISO 527-2
Elongation at Yield	8.0 %	8.0 %	ISO 527-2
Tensile Modulus	1.80 GPa	261 ksi	ISO 527-2
Flexural Modulus	1.70 GPa	247 ksi	ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m² @Temperature -20.0 °C	4.28 ft-lb/in² @Temperature -4.00 °F	ISO 180
	>= 50.0 kJ/m² @Temperature 23.0 °C	>= 23.8 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	0.500 J/cm² @Temperature -20.0 °C	2.38 ft-lb/in² @Temperature -4.00 °F	ISO 179
	>= 5.00 J/cm² @Temperature 23.0 °C	>= 23.8 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146