Total PS CPDS 815 High Flow, Non-Deca Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Total Atofina |
| Trade Name | PS CPDS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PS CPDS 815 High Flow, Non-Deca Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Total Petrochemicals Polystyrene 815 is a high heat resistant, high impact Polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensional stability.Suitable Applications for Total Petrochemicals Polystyrene 815 include TV covers.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Spiral Flow | 62.0 cm @Temperature 220 °C |
24.4 in @Temperature 428 °F |
ASTM D3123 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 89.0 µm/m-°C | 49.4 µin/in-°F | ASTM D696 |
| Vicat Softening Point | 90.0 °C @Load 1.02 kg |
194 °F @Load 2.25 lb |
50°C per hour; ASTM D1525 |
| Heat Distortion Temperature | >= 78.9 °C | >= 174 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 2.10 mm |
V-0 @Thickness 0.0827 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | ISO IEC 93 |
| Dielectric Strength | 160 kV/mm | 4060 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Polimeri Europa SINKRAL C333/m² ABS, Heat Stabilized (discontinued **)
- Loxim 830 01 HBCC Polypropylene Compound 30% Chemically Coupled, Flame Retardant
- Lehmann & Voss LUVOCOM® 1100-7725 VP Polyether sulfone, with glass fiber, lubricant modified
- Lubrizol Estane® S395A Thermoplastic Polyurethane
- ExxonMobil Escorene™ UL 00014 Ethylene Vinyl Acetate Copolymer (European Grade)
- Fainplast Compounds HAX HF 4522 Halogen Free PVC
- Covestro Makrolon® ET UV530 Polycarbonate
- CENTROPLAST CENTRODAL GF Polyoxymethylene 30% glass fiber
- Solvay Engineered Polymers DEXPRO® R210 TPV - High-Impact Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved