Polimeri Europa KOBLEND HI 40 PBT+PC, Impact Grade (discontinued **)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa KOBLEND HI 40 PBT+PC, Impact Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified blend PBT+PC blend with very good impact behaviour, ductility even at low temperatures, resistant to solvents, good dimensional stability. Main application fields: automotive industry, helmetsUnfilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³
Melt Flow	1.9 g/10 min @Load 2.16 kg, Temperature 250 °C	1.9 g/10 min @Load 4.76 lb, Temperature 482 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa	6670 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	4.6 %	4.6 %	50 mm/min
Tensile Modulus	1.80 GPa	261 ksi	1 mm/min
Izod Impact, Unnotched	NB	NB
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F
Izod Impact, Notched (ISO)	45.0 kJ/m² @Temperature -30.0 °C	21.4 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F
Deflection Temperature at 1.8 MPa (264 psi)	82.0 °C	180 °F
Vicat Softening Point	120 °C	248 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	300 V	300 V