Manifattura Cattaneo PA 6 G Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PA 6 G Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ISO 2039-2 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Conditioned 50% RH; ISO 527 |
| 80.0 MPa | 11600 psi | Dried; ISO 527 | |
| Elongation at Break | >= 40 % | >= 40 % | Dried; ISO 527 |
| >= 100 % | >= 100 % | Conditioned 50% RH; ISO 527 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | Conditioned 50% RH; ISO 527 |
| 3.10 GPa | 450 ksi | Dried; ISO 527 | |
| Flexural Strength | 140 MPa | 20300 psi | |
| 160 MPa | 23200 psi | ||
| Compressive Yield Strength | 26.0 MPa @Strain 1.00 % |
3770 psi @Strain 1.00 % |
ISO 604 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Dried; ISO 179 |
| 1.50 J/cm² | 7.14 ft-lb/in² | Conditioned 50% RH; ISO 179 | |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.21 | 0.21 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 7.5 | 7.5 | µm/s. PV = 0.1 MPa-m/s; max P = 26 MPa; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 100 °C |
44.4 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | IEC 60094 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.050 @Frequency 1.00e+6 Hz |
0.050 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | |
| UV Resistance | N | Dried |
| Y | Conditioned 50% RH |
Users viewing this material also viewed the following:
- Covestro Petlon® DP3-1039 Semi-Crystalline PET, 35% Glass Fiber (discontinued **)
- Lehmann & Voss LUVOCOM® 50-8276 Polycarbonate, with PTFE
- Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Trelleborg Fillite® SGHA (500HA) Alumino-silicate Cenospheres
- Chosun Refractories SAL75Z(ACD) Special Alumina brick
- Aremco Crystalbond™ 555 Washaway Mounting Adhesive & Accessory
- Solvay Specialty Polymers Algoflon® F5/S PTFE (Polytetrafluoroethylene) (Unverified Data**)
- LNP Lubricomp® PDX-O-97635 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE Lubricant (discontinued **)&l
- DuPont Vamac® DHC Ethylene Acrylic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved