- Polymer Property : Tensile Modulus = 6.30 GPa
Polymer Property : Tensile Modulus = 6.30 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 6.30 GPa @Thickness 0.0500 mm |
914 ksi @Thickness 0.00197 in |
ASTM D882-02 |
| NeXolve LaRC™-CP1 Conductive Black Polyimide Lower RF loss than other black and conductive black polyimides. NeXolve’s Conductive Black LaRC™-CP1 Polyimide is filled with carbon nanoparticles to produce a conductive black polyimide material .. |
|||
| Tensile Modulus | 6.30 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
914 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/1 |
| PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | same value from ASTM and ISO test. |
| BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ASTM D638 |
| Shell Carilon® DB6G6P30 Polyketone, Lubricated, Glass-Reinforced, Injection Molding Grade
(discontinued **)&l Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DA6P2L10 is a high-performance lubricated injection molding grade with mechanical properties which .. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, very good heat-ageing resistance |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527-1/-2 |
| Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | |
| LATI Latilub 66-20T G/20 PA66, 20% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218 V25 Black 21 N PA66, 25% glass fiber, Conditioned Description: TECHNYL® A 218 V25 is a polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The .. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527 Type 1A |
| Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, Conditioned Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Avail.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP DF004 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing Glass Fiber. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66 LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RKN14 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RKN14 is a compound based on Nylon 66 resin containing Mineral, MOS2. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® SHF4930 PBT (Europe-Africa-Middle East) Super high flow FR PBT grade with 15% Glass reinforced |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66 LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527-1 |
| Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber Saxalac 108 GF17 is a 17% glass fiber reinforced ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Mechanical property data te.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527 |
| Polyram Polytron P60B08-S Polypropylene, 60% Long Glass Fiber Polytron P60B08-S (Single strand) is a chemically coupled polypropylene 60% long glass fiber with extra load of additives for dilution.Information provided by Polyram. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| DSM Novamid® 1015G35 NAT PA6-GF35 35% Glass Reinforced, Injection Molding |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| DSM Novamid® 1015GH35 BK37 PA6-GF35 35% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | dry; ISO 527-1/-2 |
| EMS-Grivory Grivory® EBGM-20 HX PA666-GF15 Product description: Grilon EBGM-20 HX black 9992 is a high viscosity, high heat stabilized PA66 + PA6 extrusion blow molding grade with 15% glass fibers. The special features of Grilon EBGM-20 HX b.. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527 |
| CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1mm/min; ISO 527 |
| BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Conditioned) Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||