BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.4 % | 6.4 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | 5mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 6.30 GPa | 914 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 5.10 GPa | 740 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179 |
| 5.60 J/cm² @Temperature -30.0 °C |
26.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IFX6420Z PC (Asia Pacific)
- Chevron Phillips Marlex® HMN 55180 High Density Polyethylene (discontinued **)
- Solvay Chemicals Allyl chloride High purity – Non stabilized 3-chloropropene
- Borealis Borecene Compact™ RM8346RC Black Linear Polyethylene for Rotational Molding
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Engineered Plastics EPPC 1714C Polycarbonate
- ExxonMobil Mobil Vaculine 546
- CMW® 328 Copper Alloy
- Arlon R35948R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved