SABIC Innovative Plastics LNP Thermocomp DFZ42P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp DFZ42P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| 1.47 g/cc | 0.0531 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.29 % | 0.29 % | 23°C / 50% RH; ISO 62 |
| 0.24 % @Time 86400 sec |
0.24 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D 638 |
| 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 6.30 GPa | 914 ksi | 50 mm/min; ASTM D 638 |
| 6.60 GPa | 957 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 131 MPa | 19000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 137 MPa | 19900 psi | ISO 178 | |
| Flexural Modulus | 6.11 GPa | 886 ksi | 2 mm/min; ISO 178 |
| 6.49 GPa | 941 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.510 J/cm @Temperature 23.0 °C |
0.955 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.14 J/cm @Temperature 23.0 °C |
9.63 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² @Temperature 23.0 °C |
14.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 67.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Oceanchem Group Tris (2-chloroisopropyl) Phosphate (TCPP)
- Resinlab® EP1390 Medium Viscosity, Self Extinguishing Flame Retardant Epoxy Casting Resin System
- LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement (discontinued **)
- Lehmann & Voss LUVOCOM® 3-7088-2 Polyamide 6, with carbon fiber and glass fiber, low-warpage, heat stabilized
- Ineos Nova 1510 High Heat Crystal Polystyrene
- Lucite International Diakon® CLH952LX Acrylic Polymer
- Lushan PR298 Polypropylene Copolymer Adhesive for Steel Pipe Coating
- SSAB Tunnplat Aluzink F30A Metal-coated Mild Steel
- Hexcel® HexForce™ 332 Fiber Glass Fabric
- Axiall 7020 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved