DSM Novamid® 3021GH30 NAT PA66-GF30
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 3021GH30 NAT PA66-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Heat Stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.00 % | 2.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | cond; ISO 527-1/-2 |
| 170 MPa | 24700 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.6 % | 2.6 % | dry; ISO 527-1/-2 |
| 4.1 % | 4.1 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.30 GPa | 914 ksi | cond; ISO 527-1/-2 |
| 9.70 GPa | 1410 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 200 MPa | 29000 psi | cond; ISO 178 |
| 265 MPa | 38400 psi | dry; ISO 178 | |
| Flexural Modulus | 6.50 GPa | 943 ksi | cond; ISO 178 |
| 8.30 GPa | 1200 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 8.40 J/cm² @Temperature 23.0 °C |
40.0 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Fainplast Compounds RE 330 Rigid PVC, Extrusion
- Kazanorgsintez 107-277 Low Density Polyethylene Composition with Improved Processibility
- Lavergne VYPET VNT 840 PET 40% Glass-Mineral Reinforced
- Haynes 242® alloy, cold rolled sheet, annealed and aged
- Samsung Cheil Industries Starex® BC-0140 H ABS, Unreinforced General Purpose
- Aaron Industries AVPE LLD 300-2 Virgin Polyethylene
- Goodfellow Copper 85/Silicon 15 Alloy
- NOVA Chemicals Sclair® 99C HDPE Extrusion Resin (discontinued **)
- Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW
Copyright © lookpolymers.com All Rights Reserved