- SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 0.81 % @Time 86400 sec |
0.81 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.30 GPa | 914 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 167 MPa | 24200 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 168 MPa | 24400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Quadrant EPP Duratron® PEI U1000 PEI, unfilled, extruded (ISO Data)
- Polymer Resources PC-FR3A-D Polycarbonate, Flame Retardant, High Flow
- Gharda Chemicals GATONE™ 5600 PEEK, Low Viscosity Grade (discontinued **)
- Cookson Group Plaskon® 3400FP Epoxy Molding Compound (discontinued **)
- Styrolution PS 7800 HIPS
- Saint-Gobain CHR® C665 Copper Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- C.O.I.M. EXTER S® S 102 Orthophthalic Resin
- 3M Scotchcal™ ElectroCut™ 7725-357 Graphic Film
- SABIC Innovative Plastics LNP Stat-kon MDM40 PP
Copyright © lookpolymers.com All Rights Reserved