- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber
Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 108 GF17 Acrylonitrile Butadiene Styrene, 17% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 108 GF17 is a 17% glass fiber reinforced ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 90.0 MPa | 13100 psi | ISO 527-1 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1 |
| Tensile Modulus | 6.30 GPa | 914 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 98.0 °C @Thickness 2.00 mm |
208 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 104 °C | 219 °F | 50B; ISO 306 |
| Glow Wire Test | 750 °C | 1380 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs CE870 Ce(C2O4)3·xH2O Cerium(III) oxalate hydrate
- Qualchem Danamid AFEHUV Polyamide 66
- Polymer Resources PC-GP4-[color]-4 Polycarbonate, UV-stabilized, Easy Flow with Mold Release
- Fainplast Compounds RKS 205/K-UV Rigid PVC, Antishock Extrusion Lead Free
- Goodfellow Carbon/Epoxy Composite Sheet
- Loctite® Durabond® E-20NS Epoxy Adhesive
- Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Tubes
- A.D. Compound Adene NTTAG Copolymer 40% Talc Filled Polypropylene
- Aremco Cerama-Dip™ 538-N-BLK High Temperature Specialty Ceramic-Inorganic Coating
- Solvay Specialty Polymers Cogegum® AFR/710 Polyolefin, Unspecified (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved