PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ±0.03; DIN 53479 |
| Linear Mold Shrinkage | 0.0010 - 0.0060 cm/cm @Thickness 4.00 mm, Temperature 23.0 °C |
0.0010 - 0.0060 in/in @Thickness 0.157 in, Temperature 73.4 °F |
Flow Bergmann Method; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 170 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
24700 psi @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Elongation at Break | 3.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
3.0 % @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Tensile Modulus | 9.50 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
1380 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/1 |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 8.0 MPa | 210 °C | 410 °F | Unannealed; ISO 75-2/C |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
ALL; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Good Dimensional Stability | |
| Good Flow | ||
| Good Stiffness | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID® 6/66 FRC 3 TS PA6/66 flame retarded, heat stabilized
- Omnia Plastica Rilsan® PA6 GF - Akulon GF - at 50% RH
- ExxonMobil Escorene® LD-722 High EVA Film and Compounding Resin (discontinued **)
- SABIC Innovative Plastics SABIC PPCOMPOUND 55T1040 PP
- A. Schulman FORMION™ FI 341 Ionomer
- Williams Advanced Alloys WS243 Solder
- Chesterton OPTICOOL™ 462 Lubrication
- Daelim H&L Plavis MS Aromatic Polyimide, 15% MoS2 Filled, Machined Parts
- CMW® D55F Pre-oxidized Silver Cadmium Oxide Contact Material ASTM B781, Table 3
- Barlog Plastics KEBAFLEX SG 25 A.1 TPE-S, Shore A25, natural
Copyright © lookpolymers.com All Rights Reserved