Lanxess Durethan® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 35 HTS 901510 Nylon 6, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 35% glass fibers, very good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 6.5 % | 6.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 280 °C |
18 g/10 min @Load 11.0 lb, Temperature 536 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Conditioned; ISO 527-1/-2 |
| 190 MPa | 27600 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 8.0 % | 8.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.30 GPa | 914 ksi | Conditioned; ISO 527-1/-2 |
| 11.5 GPa | 1670 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Puncture Energy | 9.00 J | 6.64 ft-lb | ISO 6603-2 |
| 13.0 J | 9.59 ft-lb | Conditioned; ISO 6603-2 | |
| 7.00 J @Temperature -30.0 °C |
5.16 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 7.00 J @Temperature -30.0 °C |
5.16 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 140 °C | 284 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+14 ohm-cm | 7.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 5.0 @Frequency 100 Hz |
5.0 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0265 @Frequency 1.00e+6 Hz |
0.0265 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.045 @Frequency 100 Hz |
0.045 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-110,GF35 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Polymer Resources PC-GP2-D-[color]-1 Polycarbonate, General Purpose, Medium Flow with Mold Release
- DuPont Nucrel® 2940 Ethylene-Methacrylic Acid Copolymer Resin (discontinued **)
- Industeel URANUS® 65 310 L Modified Grade - Low C and Si for Nitric Acid Service
- Solvay Chemicals Sulphur Hexafluoride Technical Grade
- Teknor Apex Telcar® TL-6800-64 Thermoplastic Elastomer
- Wellman Wellamid® GF25-66 XE-N 25% Glass Fiber Reinforced, Engineering Grade Nylon 66
- Hexcel® HexWeb® HRH-36 - 1/8 - 3.0 Para-Aramid/Phenolic Core
- M Cubed Technologies ASC-701 Aluminum alloy-70% SiC Metal Matrix Composite
- Colorite Polymers CS8042SC Wire and Cable Jacket Vinyl Compound
- 3M Scotchcal™ ElectroCut™ 404 Graphic Film
Copyright © lookpolymers.com All Rights Reserved