Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 10.8 GPa | 1570 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers RIGITRON 30545 GF Polyester, 45% Glass Reinforced Polyester – 45% Glass Fiber Reinforced PET. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Var.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | (12µm polyimide/9µm copper); ASTM D882-02 |
NeXolve TR-Clad™ Flexible Polyimide Laminate The lightest weight copper clad laminates available.TR-Clad™ Flexible Laminates are both the lowest weight and lowest dielectric constant of copper/polyimide laminates available. Additionally, TR.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ASTM D638 |
LNP Thermotuf® OF-1006 HI Polyphenylene Sulfide, Glass Fiber Reinforcement
(discontinued **) Features: High Impact ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades .. |
|||
Tensile Modulus | 10.8 GPa @Temperature 100 °C |
1570 ksi @Temperature 212 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 5.0 mm/min; ASTM D638 |
Solvay Specialty Polymers KetaSpire® KT-880 GF30 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ASTM D1708 |
Solvay Specialty Polymers Torlon® 5030 Polyamide-imide (PAI)
(Unverified Data**) Torlon 5030 is a 30% glass-fiber reinforced grade of polyamide-imide (PAI) resin. It offers high strength and modulus and exceptional creep resistance. It has thermal expansion characteristics simil.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ASTM D638 |
Greene Tweed WR™ 300 PEEK, Carbon Filled WR®300 is a carbon-fiber reinforced compression molded PEEK often selected by pump manufacturers and users for pump bushings and case or impeller wear rings. Maximum service life is achieved in .. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
Lanxess Durethan® BKV 30 FN00 000000 Nylon 6, 30% Glass Fiber PA6, injection molding grade, 30% glass fibers, UL94 V-0 at 0,75 mm , free of halogen and red phosphorus, glow wire flammability test max. 960°C |
|||
Tensile Modulus | 10.8 GPa @Temperature 100 °C |
1570 ksi @Temperature 212 °F |
4; ISO 527-2 |
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high .. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON WE003ER PBT (Europe-Africa-Middle East) LNP* Stat-kon* WE003ER is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Easy Molding, Easy Release, Electrically Conductive. |
|||
Tensile Modulus | 10.8 GPa @Temperature 100 °C |
1570 ksi @Temperature 212 °F |
4; ISO 527-2 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 5 mm/min; ASTM D638 |
Solvay Specialty Polymers KetaSpire® KT-880 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber KetaSpire® KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaS.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ASTM D638 |
Plenco 1586 Polyester, Pellet, Transfer Molded PLENCO 01586 is a glass and mineral reinforced pelletized polyester molding compound offering excellent heat resistance and mechanical strength properties. This product is typically used for injecti.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
Unitika A1025GO PA6, Flame Retardant, Dry Information provided by Unitika Ltd. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527 |
BASF Ultramid® N-276 BK ND 3007 40% Glass/Mineral Filled PA66 Description: Ultramid N-276 BK ND3007 is a 40% mineral/glass reinforced, heat stabilized injection molding PA6/6.Information provided by BASF |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 |
BASF Ultramid® N-276 NF3001 40% Glass/Mineral Filled PA66 (Dry) Ultramid N-276 NF3001 is a 40% mineral/glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
Tensile Modulus | 10.8 GPa @Treatment Temp. 70.0 °C, Time 1.15e+6 sec |
1570 ksi @Treatment Temp. 158 °F, Time 320 hour |
62% rel. humidity |
Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry) Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry) Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527 |
BASF Ultramid® 1503-2F BK ND 3007 33% Glass Filled PA 66 (Dry) Description: Ultramid 1503-2F BK ND3007 is a 33% glass reinforced, heat stabilized injection molding PA6/6 grade. It is designed to provide enhance hydroysis resistance for under-the-hood applicatio.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-2 |
Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded Vydyne® R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-2 |
Ascend Performance Materials Vydyne® R633H Nylon 66/6, 33% Glass Reinforced, DAM Vydyne® R633H is 33% glass-fiber reinforced PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold .. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ASTM D638 |
LNP Thermocomp® JF-1006 Polyethersulfone, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber PA 66, injection molding grade, 35% glass fibers, black colored for laser transmission- welding (laser-transparent), good heat-ageing resistance |