BASF Ultramid® N-276 NF3001 40% Glass/Mineral Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® N-276 NF3001 40% Glass/Mineral Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid N-276 NF3001 is a 40% mineral/glass reinforced, heat stabilized injection molding nylon 6/6.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 135 MPa
19600 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
Tensile Modulus 10.8 GPa
1570 ksi
1mm/min; ISO 527
Flexural Modulus 6.90 GPa
1000 ksi
ASTM Test
9.80 GPa
1420 ksi
ISO Data
Izod Impact, Notched (ISO) 4.20 kJ/m²
2.00 ft-lb/in²
ISO Test
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
ISO 179
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.380 J/cm²
1.81 ft-lb/in²
ISO 179
0.350 J/cm²

@Temperature -30.0 °C
 1.67 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10 K/min
257 °C
495 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 241 °C
466 °F
ASTM Test
242 °C
468 °F
ISO 75
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding