BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 5.7 % | 5.7 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 193 MPa | 28000 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 210 MPa | 30500 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM Test |
| Flexural Modulus | 8.28 GPa | 1200 ksi | ASTM Test |
| 9.90 GPa | 1440 ksi | ISO Data | |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.17 mm |
2.19 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179 |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | ISO 75 |
| 297 °C | 567 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM Test |
| 255 °C | 491 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV3904 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Parker Chomerics CHO-SEAL E6306 Conductive Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT
- Solvay TECHNYL® A 208F PA66, DRY
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N990 (MT) Filler
- Corning Gorilla® Glass 3 Touch Screen Glass with NDR
- Dow Corning 200® 1000 CST FLUID
- Bulk Molding Compounds BMC 1403 Electrical Grade
- Caplinq LINQSTAT™ VCF-41014B
- Henkel Turco Liquid Sprayeze NP-LT Deoxidizer
Copyright © lookpolymers.com All Rights Reserved