- Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Automotive Applications; Automotive Electronics; Automotive Interior Parts; Automotive Under the Hood; Cell Phones; Connectors; Fuel Lines; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Transmittance - ASTM D1003 (1.60 mm): > 30 %; Transmittance - ASTM D1003 (1.60 mm): > 30 %Automotive Specifications 3M 11-0003-5762-1 X62 4200; ASTM D4000 PA121 G35 Color: BK324 Black; ASTM D4000 PA121 G35 Color: NT Natural; ASTM D6779 PA121G35; BOSCH N28 BN05-OX1 BN0510-GF35-0Anf01SO Color: NT Natural; BOSCH N28 BN05-OX1 BN0510-GF35-0Asw01SO Color: BK-324 Black; CHRYSLER MS-DB-478 CPN4242 Color: NT Natural; CHRYSLER MS-DB-478 Type A CPN3598 Color: BK324 Black; DELPHI M-53290 Color: BK324 Black; DELPHI M-53290 Color: NT Natural; DELPHI M-6071 Color: NT Natural; DELPHI MS-5216 Color: BK324 Black; DELPHI MS-5216 Color: NT Natural; FORD WSP-M4D843-A Color: BK324 Black; FORD WSP-M4D843-A Color: NT Natural; GM GMP.PPA.004 Color: BK324 Black; GM GMP.PPA.004 Color: NT Natural; GM GMW15702-110020 >PPA+GF33< (A4, A22, A64, BA633, DC1473, G20, KM1158, KS2300, LS20, RS9, SS260, Z1) Color: NT Natural; GM GMW16356P-PPA-GF35 Color: BK-324 Black; GM GMW16356P-PPA-GF35 Color: NT Natural; IMDS ID 21195756 Color: Black; IMDS ID 21195756 Color: Natural; TRW S-13318701 Color: BK543 Black; VALEO VMS-4470 Color: BK324 Black; VALEO VMS-4470 Color: NT Natural; YAZAKI YPES-25-02-135 Color: Colors; YAZAKI YPES-25-02-135 Color: NT NaturalInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa @Temperature 175 °C |
10400 psi @Temperature 347 °F |
4; ISO 527-2 |
| 80.0 MPa @Temperature 150 °C |
11600 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 148 MPa @Temperature 100 °C |
21500 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 233 MPa @Temperature 23.0 °C |
33800 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Tensile Strength | 221 MPa | 32100 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
ISO 527-2 | |
| 2.9 % @Temperature 100 °C |
2.9 % @Temperature 212 °F |
ISO 527-2 | |
| 8.5 % @Temperature 175 °C |
8.5 % @Temperature 347 °F |
ISO 527-2 | |
| 8.7 % @Temperature 150 °C |
8.7 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 13.1 GPa | 1900 ksi | ASTM D638 |
| 4.30 GPa @Temperature 175 °C |
624 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 6.70 GPa @Temperature 150 °C |
972 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 10.8 GPa @Temperature 100 °C |
1570 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 13.4 GPa @Temperature 23.0 °C |
1940 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 317 MPa | 46000 psi | ASTM D790 |
| 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
4; ISO 178 | |
| 93.0 MPa @Temperature 150 °C |
13500 psi @Temperature 302 °F |
4; ISO 178 | |
| 227 MPa @Temperature 100 °C |
32900 psi @Temperature 212 °F |
4; ISO 178 | |
| 319 MPa @Temperature 23.0 °C |
46300 psi @Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 11.4 GPa | 1650 ksi | ASTM D790 |
| 3.60 GPa @Temperature 175 °C |
522 ksi @Temperature 347 °F |
ISO 178 | |
| 4.00 GPa @Temperature 150 °C |
580 ksi @Temperature 302 °F |
ISO 178 | |
| 9.80 GPa @Temperature 100 °C |
1420 ksi @Temperature 212 °F |
ISO 178 | |
| 11.6 GPa @Temperature 23.0 °C |
1680 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 185 MPa | 26800 psi | ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Strength | 101 MPa | 14600 psi | ASTM D732 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.70 J/cm | 14.4 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.80 kJ/m² | 4.19 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 7.30 J/cm² | 34.7 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 0.950 J/cm² | 4.52 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 0.000 - 100 °C |
13.3 µin/in-°F @Temperature 32.0 - 212 °F |
2 |
| 27.0 µm/m-°C @Temperature 100 - 200 °C |
15.0 µin/in-°F @Temperature 212 - 392 °F |
2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 0.000 - 100 °C |
30.6 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 110 µm/m-°C @Temperature 100 - 200 °C |
61.1 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 313 °C | 595 °F | ISO 11357-3 |
| 313 °C | 595 °F | DSC | |
| Maximum Service Temperature, Air | 164 - 185 °C | 327 - 365 °F | Continuous Use |
| Deflection Temperature at 0.46 MPa (66 psi) | 297 °C @Thickness 3.20 mm |
567 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Unannealed; ISO 75-2/A |
| 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 4.4 @Frequency 60.0 Hz |
4.4 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.20 mm |
533 kV/in @Thickness 0.126 in |
ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 60.0 Hz |
0.0050 @Frequency 60.0 Hz |
ASTM D150 |
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 550 V | 550 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 - 318 °C | 579 - 604 °F | |
| Front Barrel Temperature | 316 - 329 °C | 601 - 624 °F | |
| Melt Temperature | 321 - 343 °C | 610 - 649 °F | |
| Mold Temperature | 135 °C | 275 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Part Marking Code | >PA6T/6I/66-GF33< | ISO 11469 |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| UL File Number | E95746 (Global) |
Users viewing this material also viewed the following:
- RheTech Products T20P200-01BG 20% Talc Reinforced Polypropylene Copolymer, General Purpose Black, Blow Molding Grade
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K BW Reinforced
- Quadrant EPP Ertacetal® H POM-H, extruded (ISO Data)
- Teknor Apex MONPRENE® MP 2720 Thermoplastic Elastomer
- Total MDPE 3802 B Medium Density Polyethylene, Cable
- Hexcel® HexForce™ 84 Carbon Fabric
- DuPont Teijin Films Melinex® 526 Polyester Film, 380 Gauge
- Arlon 15880T025 0.025" (0.635 mm) Uncured, Unsupported Silicone Rubber on a Mylar Carrier
- ACC MM918 Condensation Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved