Unitika A1025GO PA6, Flame Retardant, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1025GO PA6, Flame Retardant, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039 |
| Tensile Strength at Break | 148 MPa | 21500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527-1/-2 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.870 mm |
V-0 @Thickness 0.0343 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Parker Chomerics PREMIER™ A240-FRHF EMI Shielding Plastic
- Mearthane Durethaneâ„¢ C 50D Polyurethane
- Techmer ES HiFill® PP 0096 S LE Polypropylene
- Shinkong Synthetic Fibers Shinite® D201 PBT
- SABIC Innovative Plastics ULTEM HU2410 PEI (Asia Pacific)
- Videolar 500 Crystal Polystyrene (GPPS)
- Dow Corning JCR 6109
- Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled
- 3M 477 Vinyl Tape
Copyright © lookpolymers.com All Rights Reserved