Lanxess Durethan® BKV 30 FN00 000000 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 FN00 000000 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA6, injection molding grade, 30% glass fibers, UL94 V-0 at 0,75 mm , free of halogen and red phosphorus, glow wire flammability test max. 960°C
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.427 g/cc | 0.05155 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0022 cm/cm | 0.0022 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0062 cm/cm | 0.0062 in/in | ISO 294-4, 2577 |
| Melt Flow | 33 g/10 min @Load 2.16 kg, Temperature 260 °C |
33 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Conditioned; ISO 527-1/-2 |
| 150 MPa | 21800 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 6.1 % | 6.1 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.70 GPa | 972 ksi | Conditioned; ISO 527-1/-2 |
| 10.8 GPa | 1570 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C | 12.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C | 45.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 224 °C | 435 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 | V-0 | IEC 60695-11-10 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 | |
| 5VA @Thickness 1.60 mm |
5VA @Thickness 0.0630 in |
IEC 60695-11-20 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 36.7 kV/mm | 932 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MFR,14-110, GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 65A
- LG Chemical LUPOL GP3202 PP+MF20%
- Ipiranga Petrochem PH 1721 Polypropylene
- Lanxess Durethan® DP BC 500 H2.0 901510 Nylon 6
- SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East)
- SMAC CABLE® 2519S-10-08 Damping Material
- SABIC Innovative Plastics NORYL PX1265 PPE+PS (Asia Pacific)
- A. Schulman POLYBLAK™ 3123 Premium Black Color Concentrate, 50% Carbon Black Based In LDPE
- ChevronTexaco Transultex® CF D
- DuPont™ Surlyn® 2601 Sodium Ionomer Resin for Blown and Cast Film
Copyright © lookpolymers.com All Rights Reserved