- Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Automotive Electronics; Connectors; Electrical Parts; Electrical/Electronic ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.21 % @Time 86400 sec |
0.21 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength at Break | 72.0 MPa @Temperature 175 °C |
10400 psi @Temperature 347 °F |
4; ISO 527-2 |
| 80.0 MPa @Temperature 150 °C |
11600 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 148 MPa @Temperature 100 °C |
21500 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 233 MPa @Temperature 23.0 °C |
33800 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Tensile Strength | 221 MPa | 32100 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
ISO 527-2 | |
| 2.9 % @Temperature 100 °C |
2.9 % @Temperature 212 °F |
ISO 527-2 | |
| 8.5 % @Temperature 175 °C |
8.5 % @Temperature 347 °F |
ISO 527-2 | |
| 8.7 % @Temperature 150 °C |
8.7 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 13.1 GPa | 1900 ksi | ASTM D638 |
| 4.30 GPa @Temperature 175 °C |
624 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 6.70 GPa @Temperature 150 °C |
972 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 10.8 GPa @Temperature 100 °C |
1570 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 13.4 GPa @Temperature 23.0 °C |
1940 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 317 MPa | 46000 psi | ASTM D790 |
| 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
4; ISO 178 | |
| 93.0 MPa @Temperature 150 °C |
13500 psi @Temperature 302 °F |
4; ISO 178 | |
| 227 MPa @Temperature 100 °C |
32900 psi @Temperature 212 °F |
4; ISO 178 | |
| 319 MPa @Temperature 23.0 °C |
46300 psi @Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 11.4 GPa | 1650 ksi | ASTM D790 |
| 3.60 GPa @Temperature 175 °C |
522 ksi @Temperature 347 °F |
ISO 178 | |
| 4.00 GPa @Temperature 150 °C |
580 ksi @Temperature 302 °F |
ISO 178 | |
| 9.80 GPa @Temperature 100 °C |
1420 ksi @Temperature 212 °F |
ISO 178 | |
| 11.6 GPa @Temperature 23.0 °C |
1680 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 185 MPa | 26800 psi | ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Strength | 101 MPa | 14600 psi | ASTM D732 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.70 J/cm | 14.4 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.80 kJ/m² | 4.19 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 7.30 J/cm² | 34.7 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 0.950 J/cm² | 4.52 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 0.000 - 100 °C |
13.3 µin/in-°F @Temperature 32.0 - 212 °F |
2 |
| 27.0 µm/m-°C @Temperature 100 - 200 °C |
15.0 µin/in-°F @Temperature 212 - 392 °F |
2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 0.000 - 100 °C |
30.6 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 110 µm/m-°C @Temperature 100 - 200 °C |
61.1 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 313 °C | 595 °F | ISO 11357-3 |
| 313 °C | 595 °F | DSC | |
| Maximum Service Temperature, Air | 164 - 185 °C | 327 - 365 °F | Continuous Use |
| Deflection Temperature at 0.46 MPa (66 psi) | 297 °C @Thickness 3.20 mm |
567 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Unannealed; ISO 75-2/A |
| 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 4.4 @Frequency 60.0 Hz |
4.4 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.20 mm |
533 kV/in @Thickness 0.126 in |
ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 60.0 Hz |
0.0050 @Frequency 60.0 Hz |
ASTM D150 |
| 0.017 @Frequency 1.00e+6 Hz |
0.017 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 550 V | 550 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 - 318 °C | 579 - 604 °F | |
| Front Barrel Temperature | 316 - 329 °C | 601 - 624 °F | |
| Melt Temperature | 321 - 343 °C | 610 - 649 °F | |
| Mold Temperature | 135 °C | 275 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Part Marking Code | >PA6T/6I/66-GF33< | ISO 11469 |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Rogers Corporation TMM® TMM10 Ceramic Thermoset Polymer Composite
- SABIC Innovative Plastics Cycoloy® CX7211 PC+ABS
- Overview of materials for Nylon 66, 30% Mineral Filled
- Lanxess Pocan® BF 4215 000000 PBT, 12% Glass Fiber
- Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Conditioned)
- Teknor Apex Flexalloy® 9100-45 Polyvinyl Chloride Elastomer
- Fainplast Compounds GK 90/R Flexible PVC, Flame Retardant Sheathing Lead Free
- ChevronTexaco Dura-Lith® NLGI 0 Grease EP
- 3M Scotch-Weld™ DP8405NS Acrylic Adhesives
- Quantum Composites QC-8704 63% Glass Fiber Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved