BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1503-2 BK ND3007 33% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1503-2 BK ND3007 is a 33% glass reinforced, heat stabilized, pigmented black injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 5.7 % | 5.7 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 283 MPa | 41000 psi | ASTM Test |
| Flexural Modulus | 8.28 GPa | 1200 ksi | ASTM Test |
| 9.90 GPa | 1440 ksi | ISO Data | |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.17 mm |
2.19 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO Test |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | ISO 75 |
| 297 °C | 567 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM Test |
| 255 °C | 491 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products P601-01 Polypropylene Copolymer, Black
- DSM Akulon® K230-HXG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond) (discontinued **)
- Solvay Specialty Polymers KetaSpire® KT-880 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber
- Plastics Group Polifil® GFPP-30 30% Glass-Reinforced Polypropylene
- Hippe PF CP 42 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Arlon 25188T017 Silicone Rubber/Laminated ETFE Film
- Bhansali Engineering Abstron TIM 300 MMA- ABS
- Resistalloy International Fecralloy™ Electrical Resistance Steel
Copyright © lookpolymers.com All Rights Reserved